Crystallinity / Degree of Crystallinity

Crystallinity refers to the degree of structural order of a solid. In a crystal, the arrangement of atoms or molecules is consistent and repetitive. Many materials such as glass ceramics and some polymers can be prepared in such a way as to produce a mixture of crystalline and amorphous regions.

However, even for completely crystalline materials, the degree of structural perfection can vary.

For example, most metallic alloys are crystalline, but usually comprise many independent crystalline regions (grains or crystallites).

In various orientations separated by grain boundaries, they also contain other crystallographic defects, such as dislocations. That reduces the degree of structural perfection.

The most highly perfect crystals are silicon boules produced for semiconductor electronics which are large single crystals (i.e., they have no grain boundaries); these are nearly free of dislocations and have precisely controlled concentrations of defect atoms.

Crystallization of polymers can be observed in some thermoplastics. When the melt solidifies, partial alignment of the molecular chains in the polymer occurs. Based on crystallization nuclei, the molecular chains fold together and form ordered regions called lamellae.

Degree of Crystallinity

The properties of plastics are significantly influenced by their degree of crystallization. The higher the degree of crystallization, the stiffer and stronger, but also more brittle a molded part is.

The degree of crystallization is influenced by the chemical structure and thermal history, such as the cooling conditions during processing or post-thermal treatment.

For determination of the degree of crystallization, K, the measured melting enthalpy ∆Hmeas is set in relation to the literature value ∆Hlit for completely crystalline material.

K= ∆Hmeas / ∆Hlit

Thermal history: The thermal or mechanical history is shown in the 1st heating curve of a DSC measurement. The 2nd heating curve serves for determination of the material properties under given dynamic conditions.

The degree of crystallinity has a significant influence on hardness, density, transparency and diffusion.

However, the properties are not determined only by the degree of crystallinity, but also by the size of the structural units or the molecular orientation.

Application Examples

Determination of the degree of crystallinity of polymers

The melting behavior of low-density polyethylene (LDPE), high-density polyethylene (HDPE) and polypropylene (PP) is depicted in figure 2.

Peak temperatures help in identifying polymers and polymer mixtures.

The peak areas represent the melting enthalpies.

Based on these values from the experiment, the degree of crystallinity can be determined by means of the standard Proteus evaluation software.

The melting enthalpy for 100% crystalline PE is 293 J/g and is 207 J/g for PP. This yields a calculated crystallinity for LDPE of 46.5%, for HDPE of 74.2% and for PP of 48.8%.

Fig. 2: Determination of the degree of crystallization for different polymers between RT and 200°C at a heating rate of 10 K/min in a nitrogen atmosphere (40 ml/min); the measurements were carried out with the DSC 204 F1 Phoenix® employing alumina crucibles with pierced lids.

Determination of the degree of Crystallinity during Post Crystallization

The calculation of the degree of crystallinity, K, of PET is depicted in figure 3 below.

At this point, the enthalpy area of the melt, ∆hm, here 42.83 J/g, is subtracted from the enthalpy area of the post-crystallization, ∆hc, here 40.29 J/g, and divided by the literature value of 140 J/g.

This results in a degree of crystallization, K, of 1.8% for PET.

Application Note

Fig. 3: Calculation of the Degree of Crystallization, K, during post-crystallization of PET in the temperature range between RT and 300°C. The sample was heated at a heating rate of 10 K/min in a sealed alumina crucible with pierced lid.