Glass Fiber Reinforced PBT — Dynamic-Mechanical Properties

A 30% glass fiber-reinforced PBT (parallel and perpendicular to the fiber orientation) was measured in the 3-point bending mode at 1 Hz and 2 K/min. Considerably higher values for the stiffness and the onset of the E'-decrease (43°C) are obtained for the parallel-oriented type (solid line). The tanδ values are accordingly lower. The tanδ peaks are at the same temperature.

The polyester fiber tested in the tension mode shows relaxations in the low-temperature range, which can be evaluated at E' onset, E'' peak or tanδ peak. Glass transition starts at 75°C. The storage modulus decreased from approx. 4,200 MPa to 200 MPa. (measurement with DMA 242 E Artemis)

DMA 242 D - Dynamic mechanical Analyzer

The robust construction of the DMA 242 D and the high resolution of the deformation measuring system enable precise measurements on both very rigid and very soft samples. The most varied of deformation types, digital signal filtering, kinetic evaluation and frequency extrapolation make the DMA 242 D to a real all-rounder.

DMA 242 E Artemis

DMA 242 E Artemis’in sağlam yapısı ve yüksek çözünürlüklü deformasyon ölçüm sistemi hem rijit hem de yumuşak numunelerde hassas ölçüme imkan tanımaktadır. Çok çeşitli deformasyon tipleri, dijital sinyal filtreleme, kinetik değerlendirme ve frekans ektrapolasyonu DMA 242 E Artemis’i gerçekten çok marifetli bir cihaz yapmaktadır.